Beryllium Copper Strip Products
Mechanical Properties
Temper Standard | Temper ASTM | Age Hardened Condition | 0.2% Yield Strength ksi | Tensile Strength ksi | Elongation % in 2" | Hardness DPH | Hardness Rockwell B or C |
---|---|---|---|---|---|---|---|
BERYLCO ALLOY 165 (UNS C17000); 1.75 wt% Be, 0.25 wt% Co, Balance Cu | |||||||
A 1/4H 1/2H H |
TB00 TD01 TD02 TD04 |
— — — — |
28-60 60-80 75-95 90-112 |
60-78 75-88 85-100 100-130 |
35-65 15-40 12-30 2-10 |
90-150 120-180 180-225 215-280 |
B45-78 B68-90 B88-96 B96-104 |
AT 1/4HT 1/2HT HT |
TF00 TH01 TH02 TH04 |
600°F/3 hr 600°F/2 hr 600°F/2 hr 600°F/2 hr |
130-165 135-170 145-175 155-185 |
150-180 160-190 170-200 180-210 |
3-15 3-10 1-8 1-6 |
345 min. 355 min. 365 min. 375 min. |
C33 min. C35 min. C37 min. C38 min. |
AM 1/4HM 1/2HM HM SHM XHM |
TM00 TM01 TM02 TM04 TM05 TM06 |
Mill-hardened Mill-hardened Mill-hardened Mill-hardened Mill-hardened Mill-hardened |
70-95 80-110 95-125 110-135 125-140 135-165 |
100 min. 110 min. 120 min. 135 min. 150 min. 155 min. |
18-30 15-25 12-22 9-20 9-18 3-10 |
205 min. 225 min. 245 min. 280 min. 310 min. 350 min. |
B95 min. C20 min. C24 min. C28 min. C31 min. C32 min. |
BERYLCO ALLOY 25 (UNS C17200); 1.85 wt% Be, 0.25 wt% Co, Balance Cu | |||||||
A 1/4H 1/2H H |
TB00 TD01 TD02 TD04 |
— — — — |
28-60 60-80 75-95 90-112 |
60-78 75-88 85-100 100-130 |
35-65 15-40 9-30 2-18 |
90-150 120-180 180-225 215-280 |
B45-78 B68-90 B88-96 B96-104 |
AT 1/4HT 1/2HT HT |
TF00 TH01 TH02 TH04 |
600°F/3 hr 600°F/2 hr 600°F/2 hr 600°F/2 hr |
140-175 150-185 160-195 165-205 |
165-195 175-205 185-215 190-220 |
3-15 3-10 1-8 1-6 |
360 min. 370 min. 380 min. 390 min. |
C36 min. C36 min. C38 min. C38 min. |
AM 1/4HM 1/2HM HM SHM XHM XHMS |
TM00 TM01 TM02 TM04 TM05 TM06 TM08 |
Mill-hardened Mill-hardened Mill-hardened Mill-hardened Mill-hardened Mill-hardened Mill-hardened |
70-95 80-110 95-125 110-135 125-140 135-165 150-180 |
100 min. 110 min. 120 min. 135 min. 150 min. 155 min. 175 min. |
16-30 15-25 12-22 9-20 9-18 4-15 3-12 |
205 min. 225 min. 245 min. 280 min. 310 min. 350 min. 370 min. |
B95 min. C20 min. C23 min. C28 min. C31 min. C32 min. C33 min. |
BERYLCO ALLOY 14 (UNS C17510); 0.50 wt% Be, 1.80 wt% Ni, Balance Cu | |||||||
A H |
TB00 TD04 |
— — |
20-40 55-80 |
35-55 70-85 |
20-35 2-8 |
65-130 125-180 |
B20-45 B78-88 |
AT HT |
TF00 TH04 |
850-900°F/3 hr 850-900°F/2 hr |
80-110 95-130 |
100-130 110-140 |
8-20 5-15 |
195-270 220-290 |
B92-100 B95-102 |
BERYLCO ALLOY 17510TMP (UNS C17510); 0.50 wt% Be, 1.80 wt% Ni, Balance Cu | |||||||
1/2HM HM |
TM02 TM04 |
MIll-hardened MIll-hardened |
85-110 100-125 |
95-120 100-135 |
10 min. 6 min. |
230 254 |
B96 B100 |